Yasin Standard Black PA6 CF Black
MaterialID MAT0024
3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:12:06
48/100
7/8
20 / 80
32.96
Engineering profile
Recommended applications
- Rigid brackets, fixtures and shape-stable prototypes
- Repeatable print jobs and production-style batches
- Cosmetic parts, concept models or low-load prototypes
- Avoid high impact components
Measured strengths
- Consistency: 82/100. Repeatability is one of the stronger signals in this material profile.
- Stiffness: 100/100. Stiffness is a relative advantage in this comparison group.
Limitations
- Izod/Charpy impact family: 7/100. Validate impact or shock-loaded components against their application requirements.
- Layer adhesion: 10/100. Z-axis performance should be treated with caution.
Engineering trade-offs
- Stiffness is useful for shape stability, but impact tolerance is a separate limitation.
- The report should be read as a suitability warning rather than a general-purpose recommendation.
Base-material printing guidance
| Guidance | Minimum | Recommended | Maximum | Unit |
|---|---|---|---|---|
| Nozzle temperature | 280 | 280 | 295 | °C |
| Bed temperature | 105 | 110 | 110 | °C |
| Print speed | 11 | 65 | 65 | mm/s |
| Cooling | 10 | 10 | 15 | % |
| Guidance | Value | Unit |
|---|---|---|
| Cooling guidance | Low | |
| Drying temperature | 100 | °C |
| Drying time | 12 | hours |
| Enclosure | Required | |
| Printer / G-code reference | PrusaCoreOneL | |
| Slicer profile reference | Yasin PA6 |
Print workflow checks
- Confirm nozzle temperature, bed temperature, speed, cooling and drying requirements from the manufacturer profile or spool label.
- Print a small validation part before committing to a long, costly or safety-relevant print.
- Orient the part so the governing load does not rely on an unverified or weak engineering axis.
- Reinforced filament: confirm an abrasion-resistant nozzle and manufacturer drying/storage requirements.
- Engineering/high-temperature family: confirm enclosure, ventilation, warping control and material-specific drying requirements.
- Layer-adhesion evidence is weak; avoid critical Z-axis loading without additional validation.
Decision guidance
- Use this material mainly for low-load, visual or experimental parts.
- Review the listed alternatives if the application needs stronger overall performance.
- Validate impact-focused or shock-loaded designs against the measured Izod/Charpy results.
Stronger same-family alternatives
| MaterialID | Material | Manufacturer | Overall | Tensile | Impact | Izod | Charpy |
|---|---|---|---|---|---|---|---|
| MAT0023 | Extrudr DuraPro PA6 CF Black | Extrudr | 52/100 | 52/100 | — | n/a | n/a |
| MAT0025 | Extrudr DuraPro PA6 GF Black | Extrudr | 52/100 | 47/100 | — | n/a | n/a |
| MAT0248 | Bedrock 3D Standard Black PA6 HighTemp CF Black | Bedrock 3D | 51/100 | 48/100 | — | n/a | n/a |
Testing methodology · Download PDF
Izod and Charpy Impact Strength
Izod Impact Strength · 2026-10-01
Instrument readings in kJ/m²
Mean 5.898 kJ/m²; Std. Dev 0.458 kJ/m²; CV 7.76%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Charpy Impact Strength · 2026-10-01
Instrument readings in kJ/m²
Mean 5.716 kJ/m²; Std. Dev 0.316 kJ/m²; CV 5.535%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.