Public printing recommendation
Prima Creator PrimaSelect Dark Blue PLA Blue
MaterialID MAT0113
3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:12:06
Guidance boundary: values below are shared base-material guidance resolved only through the canonical BaseMaterialId link. They are not manufacturer-, spool- or printer-specific validated settings. Missing fields remain Not recorded.
Overall
—
—
Engineering axes
5/8
5/8
Public rank
—
—
MSRP USD/kg
20.78
20.78
Engineering profile
Recommended applications
- Rigid brackets, fixtures and shape-stable prototypes
- Repeatable print jobs and production-style batches
- Cosmetic parts, concept models or low-load prototypes
- Avoid high tensile load applications
Measured strengths
- Consistency: 73/100. Repeatability is one of the stronger signals in this material profile.
- Stiffness: 92/100. Stiffness is a relative advantage in this comparison group.
Limitations
- Tensile: 34/100. Avoid using this as the primary choice for tensile-loaded parts.
- Layer adhesion: 23/100. Z-axis performance should be treated with caution.
Engineering trade-offs
- Good repeatability does not compensate for low tensile capability in load-bearing designs.
Base-material printing guidance
| Guidance | Minimum | Recommended | Maximum | Unit |
|---|---|---|---|---|
| Nozzle temperature | 195 | 230 | 230 | °C |
| Bed temperature | 60 | 60 | 70 | °C |
| Print speed | 55 | 165 | 165 | mm/s |
| Cooling | 20 | 80 | 85 | % |
| Guidance | Value | Unit |
|---|---|---|
| Cooling guidance | High | |
| Drying temperature | 50 | °C |
| Drying time | 5 | hours |
| Enclosure | Not required | |
| Printer / G-code reference | PrusaCoreOneL | |
| Slicer profile reference | Prusament PLA |
Print workflow checks
- Confirm nozzle temperature, bed temperature, speed, cooling and drying requirements from the manufacturer profile or spool label.
- Print a small validation part before committing to a long, costly or safety-relevant print.
- Orient the part so the governing load does not rely on an unverified or weak engineering axis.
- Layer-adhesion evidence is weak; avoid critical Z-axis loading without additional validation.
Decision guidance
- Overall suitability is unavailable until the required measurements and method references are complete.
- Do not choose it as a tensile-strength benchmark material.
Stronger same-family alternatives
| MaterialID | Material | Manufacturer | Overall | Tensile | Impact | Izod | Charpy |
|---|
Confirm exact settings against the manufacturer profile, spool label and actual printer/material combination. Results do not replace application-specific validation.
Testing methodology · Download PDF
Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.