Public printing recommendation
Yasin Standard White HIPS White
MaterialID MAT0240
3DPIceland Labs
Generated with 3DPIceland Engineering Platform v60.0.6 WORKFLOW-RELIABILITY - Bug Fixes and Workflow Reliability
2026-08-25 19:05:46
Guidance boundary: values below are shared base-material guidance resolved only through the canonical BaseMaterialId link. They are not manufacturer-, spool- or printer-specific validated settings. Missing fields remain Not recorded.
Overall
40/100
40/100
Engineering axes
6/5
6/5
Public rank
201 / 234
201 / 234
MSRP USD/kg
26.88
26.88
Engineering profile
Recommended applications
- Cosmetic parts, concept models or low-load prototypes
- Avoid high tensile load applications
Measured strengths
- Best available signal: Consistency at 70/100.
Limitations
- Tensile: 12/100. Avoid using this as the primary choice for tensile-loaded parts.
- Layer adhesion: 11/100. Z-axis performance should be treated with caution.
Engineering trade-offs
- Good repeatability does not compensate for low tensile capability in load-bearing designs.
- The report should be read as a suitability warning rather than a general-purpose recommendation.
Base-material printing guidance
| Guidance | Minimum | Recommended | Maximum | Unit |
|---|---|---|---|---|
| Nozzle temperature | 220 | 230 | 235 | °C |
| Bed temperature | 110 | 110 | 120 | °C |
| Print speed | 55 | 165 | 165 | mm/s |
| Cooling | 15 | 20 | 20 | % |
| Guidance | Value | Unit |
|---|---|---|
| Cooling guidance | Low | |
| Drying temperature | 75 | °C |
| Drying time | 6 | hours |
| Enclosure | Required | |
| Printer / G-code reference | PrusaCoreOneL | |
| Slicer profile reference | Generic HIPS |
Print workflow checks
- Confirm nozzle temperature, bed temperature, speed, cooling and drying requirements from the manufacturer profile or spool label.
- Print a small validation part before committing to a long, costly or safety-relevant print.
- Orient the part so the governing load does not rely on an unverified or weak engineering axis.
- Layer-adhesion evidence is weak; avoid critical Z-axis loading without additional validation.
Decision guidance
- Use this material mainly for low-load, visual or experimental parts.
- Do not choose it as a tensile-strength benchmark material.
Stronger same-family alternatives
| MaterialID | Material | Manufacturer | Overall | Tensile | Impact |
|---|
Confirm exact settings against the manufacturer profile, spool label and actual printer/material combination. Results do not replace application-specific validation.