Bedrock 3D Standard Black ABS Plus Black

MaterialID MAT0246

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:12:06

Guidance boundary: values below are shared base-material guidance resolved only through the canonical BaseMaterialId link. They are not manufacturer-, spool- or printer-specific validated settings. Missing fields remain Not recorded.

Overall
46/100

Engineering axes
7/8

Public rank
28 / 80

MSRP USD/kg
31.81

Engineering profile

Overall

46/100

Tensile

14/100

Impact

—

Izod

82/100

Charpy

100/100

Stiffness

36/100

Consistency

81/100

Layer adhesion

10/100

Recommended applications

Impact-aware parts where toughness matters
Repeatable print jobs and production-style batches
Cosmetic parts, concept models or low-load prototypes
Avoid high tensile load applications

Measured strengths

Consistency: 81/100. Repeatability is one of the stronger signals in this material profile.
Izod/Charpy impact family: 91/100. The two-method impact score is competitive against the material-family context.

Limitations

Tensile: 14/100. Avoid using this as the primary choice for tensile-loaded parts.
Stiffness: 36/100. Expect less shape stability than the stronger materials in the same family.
Layer adhesion: 10/100. Z-axis performance should be treated with caution.

Engineering trade-offs

Good repeatability does not compensate for low tensile capability in load-bearing designs.
The report should be read as a suitability warning rather than a general-purpose recommendation.

Base-material printing guidance

Guidance	Minimum	Recommended	Maximum	Unit
Nozzle temperature	250	255	265	°C
Bed temperature	110	110	110	°C
Print speed	55	165	165	mm/s
Cooling	15	20	20	%

Guidance	Value	Unit
Cooling guidance	Low
Drying temperature	75	°C
Drying time	6	hours
Enclosure	Required
Printer / G-code reference	PrusaCoreOneL
Slicer profile reference	Prusa Buddy3D ABS

Print workflow checks

Confirm nozzle temperature, bed temperature, speed, cooling and drying requirements from the manufacturer profile or spool label.
Print a small validation part before committing to a long, costly or safety-relevant print.
Orient the part so the governing load does not rely on an unverified or weak engineering axis.
Engineering/high-temperature family: confirm enclosure, ventilation, warping control and material-specific drying requirements.
Layer-adhesion evidence is weak; avoid critical Z-axis loading without additional validation.

Decision guidance

Use this material mainly for low-load, visual or experimental parts.
Do not choose it as a tensile-strength benchmark material.

Stronger same-family alternatives

MaterialID	Material	Manufacturer	Overall	Tensile	Impact	Izod	Charpy

Confirm exact settings against the manufacturer profile, spool label and actual printer/material combination. Results do not replace application-specific validation.

Testing methodology · Download PDF

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-09-29
Instrument readings in kJ/m²
Mean 65.708 kJ/m²; Std. Dev 9.686 kJ/m²; CV 14.741%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-09-29
Instrument readings in kJ/m²
Mean 123.714 kJ/m²; Std. Dev 9.88 kJ/m²; CV 7.986%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.