Public test session report

Prusa3D Buddy3D PLA Silk Black

MaterialID MAT0082

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	Not recorded
Charpy	Not recorded
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
41

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	5,229 MPa	2,692 MPa	0,515%	10	10/10	OK
Tensile	Flat	37,821 MPa	12,832 MPa	0,339%	10	10/10	OK
Impact	Upright	5,304 kJ/m²	0,806 kJ/m²	0,152%	10	10/10	OK
Impact	Flat	11,034 kJ/m²	0,956 kJ/m²	0,087%	10	10/10	OK
Stiffness	Three-point bend	2753,914 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	13, 68, 41, 30, 23, 47, 50, 24, 13, 31
Tensile	Flat force inputs (N)	345, 132, 335, 337, 198, 169, 163, 269, 193, 318
Impact	Upright needle inputs (%)	6,00, 5,00, 5,50, 7,00, 6,50, 8,00, 6,00, 7,00, 8,00, 6,50
Impact	Flat needle inputs (%)	12,50, 14,00, 14,00, 11,00, 14,00, 13,00, 15,00, 14,00, 13,00, 14,50
Stiffness	Revolutions / degrees	1 / 310

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF