Public test session report

Prusa3D Prusament Oh My Gold PLA Silk Gold

MaterialID MAT0087

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	2026-09-30
Charpy	2026-09-30
Stiffness	Not recorded

Rigid test status
Complete

Rigid result modules
6/6

Rigid specimen/result records
40

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	7,725 MPa	2,467 MPa	0,319%	9	9/10	OK
Tensile	Flat	46,235 MPa	2,713 MPa	0,059%	10	10/10	OK
Impact	Upright	3,023 kJ/m²	1,151 kJ/m²	0,381%	10	10/10	OK
Impact	Flat	11,241 kJ/m²	0,71 kJ/m²	0,063%	10	10/10	OK
Stiffness	Three-point bend	2145,491 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	43, 35, 48, 45, 36, 79, 35, 63, 68,
Tensile	Flat force inputs (N)	311, 313, 323, 293, 304, 295, 305, 309, 258, 295
Impact	Upright needle inputs (%)	2,00, 3,00, 3,50, 4,00, 4,50, 5,00, 6,00, 3,00, 1,50, 5,00
Impact	Flat needle inputs (%)	13,00, 14,50, 14,00, 14,00, 15,00, 12,50, 13,50, 12,50, 14,00, 14,50
Stiffness	Revolutions / degrees	2 / 140

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 4.782 kJ/m²; Std. Dev 0.289 kJ/m²; CV 6.039%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 5.851 kJ/m²; Std. Dev 1.307 kJ/m²; CV 22.331%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.