Public test session report

Yasin Standard Soft PLA PLA Soft White

MaterialID MAT0094

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	2026-10-03
Charpy	2026-10-03
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
39

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	3,623 MPa	0,796 MPa	0,22%	9	9/10	OK
Tensile	Flat	9,751 MPa	1,071 MPa	0,11%	10	10/10	OK
Impact	Upright	7,985 kJ/m²	3,67 kJ/m²	0,46%	10	10/10	OK
Impact	Flat	36,225 kJ/m²	3,575 kJ/m²	0,099%	10	10/10	OK
Stiffness	Three-point bend	n/a	n/a	n/a	0		OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	16, 21, 22, 22, 30, 29, 20, 21, 31,
Tensile	Flat force inputs (N)	64, 67, 64, 66, 65, 68, 67, 44, 64, 65
Impact	Upright needle inputs (%)	8,00, 5,50, 15,00, 7,00, 7,00, 14,00, 9,00, 4,50, 10,00, 18,00
Impact	Flat needle inputs (%)	51,00, 42,00, 44,00, 44,00, 40,00, 52,00, 37,00, 50,00, 47,00, 50,00
Stiffness	Revolutions / degrees

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF

Flexible Material Testing

Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.

Method	Result	Condition	Mean	n	SD	CV %	Range
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	10 s hold · 2 mm displacement · cycle 1	6.262	10	0.106	1.691	6.099–6.413
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	30 s hold · 2 mm displacement · cycle 1	6.046	10	0.095	1.571	5.879–6.193
eaacea91	Compression Force at 20% Strain (N)	10 s hold · 2 mm displacement · cycle 1	398.4	10	6.736	1.691	388–408
eaacea91	Compression Force at 20% Strain (N)	30 s hold · 2 mm displacement · cycle 1	384.6	10	6.041	1.571	374–394
eaacea91	Force reduction from 10 s to 30 s at 20% Strain (%)	first compression only · 2 mm displacement	3.462	10	0.302	8.737	2.813–3.769
eaacea91	Force retention at 20% Strain (%)	10–30 s · 2 mm displacement · cycle 1	96.538	10	0.302	0.313	96.231–97.187
eaacea91	Residual height loss after recovery (%)	20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1	4.06	10	0.158	3.886	3.7–4.3
ed381ba8	Shore A Hardness (Shore A)	10 s reading · 8 mm	93	1	—	—	93–93

Shore location statistics

Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.

Method	Scale	Condition	Specimen	Readings	Mean	Location SD	Location CV %
ed381ba8	Shore A Hardness	10 s reading · 8 mm	1	5	93	2.031	2.184

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 39.349 kJ/m²; Std. Dev 3.768 kJ/m²; CV 9.576%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 26.715 kJ/m²; Std. Dev 2.097 kJ/m²; CV 7.851%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.