Public test session report

Extrudr BioFusion Blue Fire PLA Blue

MaterialID MAT0115

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v60.0.6 WORKFLOW-RELIABILITY - Bug Fixes and Workflow Reliability
2026-08-25 19:04:35

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Stiffness	Not recorded

Status
Complete

Result modules
3/3

Specimen/result records
37

Public details
Approved

Specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	1,252 MPa	0,287 MPa	0,229%	7	7/10	OK
Tensile	Flat	33,115 MPa	9,785 MPa	0,295%	10	10/10	OK
Impact	Upright	155,337 kJ/m²	13,492 kJ/m²	0,087%	10	10/10	OK
Impact	Flat	354,506 kJ/m²	83,682 kJ/m²	0,236%	9	9/10	OK
Stiffness	Three-point bend	2527,565 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	9, 5, 10, 9, 7, 7, 10, , ,
Tensile	Flat force inputs (N)	209, 200, 185, 186, 248, 219, 356, 236, 213, 101
Impact	Upright needle inputs (%)	9,00, 9,00, 9,00, 8,00, 8,00, 10,00, 10,00, 10,00, 10,00, 9,00
Impact	Flat needle inputs (%)	22,00, 25,00, 17,00, 31,00, 14,50, 19,00, 17,00, 21,00, 21,00,
Stiffness	Revolutions / degrees	2 / 10

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF