Public test session report

Add:North Enhanced PLA Natural

MaterialID MAT0134

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	Not recorded
Charpy	Not recorded
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
2/6

Rigid specimen/result records
40

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	24,163 MPa	2,838 MPa	0,117%	10	10/10	OK
Tensile	Flat	39,882 MPa	1,646 MPa	0,041%	10	10/10	OK
Impact	Upright	2,17 kJ/m²	0,341 kJ/m²	0,157%	10	10/10	OK
Impact	Flat	7,935 kJ/m²	0,759 kJ/m²	0,096%	10	10/10	OK
Stiffness	Three-point bend	n/a	n/a	n/a	0		OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	155, 166, 152, 111, 153, 172, 162, 153, 176, 171
Tensile	Flat force inputs (N)	277, 263, 246, 271, 264, 253, 261, 264, 247, 247
Impact	Upright needle inputs (%)	2,00, 3,00, 3,00, 2,00, 3,00, 2,50, 3,00, 3,00, 2,50, 3,00
Impact	Flat needle inputs (%)	11,00, 8,00, 9,50, 11,00, 10,00, 10,00, 9,00, 10,00, 10,00, 9,00
Stiffness	Revolutions / degrees

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF