Public test session report

Thorwell Standard HIPS HIPS Blue

MaterialID MAT0146

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	Not recorded
Charpy	Not recorded
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
33

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	2,192 MPa	0,715 MPa	0,326%	4	4/10	OK
Tensile	Flat	19,995 MPa	4,734 MPa	0,237%	10	10/10	OK
Impact	Upright	5,932 kJ/m²	1,694 kJ/m²	0,285%	8	8/10	OK
Impact	Flat	29,502 kJ/m²	1,904 kJ/m²	0,065%	10	10/10	OK
Stiffness	Three-point bend	1882,778 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	16, 19, 8, 14, , , , , ,
Tensile	Flat force inputs (N)	141, 145, 143, 148, 160, 88, 153, 131, 128, 63
Impact	Upright needle inputs (%)	3,50, 8,50, 7,00, 5,00, 8,00, 9,50, 8,00, 9,00, ,
Impact	Flat needle inputs (%)	32,00, 35,00, 35,00, 37,00, 36,00, 38,00, 36,00, 35,00, 41,00, 39,00
Stiffness	Revolutions / degrees	2 / 260

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF