Public test session report

Sunlu Standard Red PLA High Speed Red

MaterialID MAT0185

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	Not recorded
Charpy	Not recorded
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
41

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	7,183 MPa	3,615 MPa	0,503%	10	10/10	OK
Tensile	Flat	41,39 MPa	4,748 MPa	0,115%	10	10/10	OK
Impact	Upright	7,646 kJ/m²	0,608 kJ/m²	0,08%	10	10/10	OK
Impact	Flat	15,212 kJ/m²	1,514 kJ/m²	0,1%	10	10/10	OK
Stiffness	Three-point bend	2816,981 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	59, 88, 41, 22, 67, 18, 27, 36, 37, 72
Tensile	Flat force inputs (N)	290, 281, 206, 293, 227, 264, 263, 304, 288, 275
Impact	Upright needle inputs (%)	9,5, 10, 8,5, 9, 10, 10, 9, 10, 10, 8
Impact	Flat needle inputs (%)	19, 16, 20, 19, 18,5, 18, 15, 21, 19, 20
Stiffness	Revolutions / degrees	1 / 295

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF