Public test session report

Sunlu Standard Black PLA High Speed Black

MaterialID MAT0187

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	Not recorded
Charpy	Not recorded
Stiffness	Not recorded

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
41

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	4,199 MPa	2,635 MPa	0,628%	10	10/10	OK
Tensile	Flat	41,359 MPa	5,283 MPa	0,128%	10	10/10	OK
Impact	Upright	8,224 kJ/m²	1,045 kJ/m²	0,127%	10	10/10	OK
Impact	Flat	17,517 kJ/m²	1,573 kJ/m²	0,09%	10	10/10	OK
Stiffness	Three-point bend	3127,326 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	16, 44, 41, 26, 59, 10, 22, 11, 36, 8
Tensile	Flat force inputs (N)	288, 251, 255, 283, 303, 201, 271, 302, 304, 231
Impact	Upright needle inputs (%)	10, 9,5, 9,5, 13,5, 9,5, 10, 9, 10, 10,5, 9,5
Impact	Flat needle inputs (%)	23, 22, 24, 24, 21, 21, 19, 21, 20, 18,5
Stiffness	Revolutions / degrees	1 / 230

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF