Public test session report

Eryone Standard Black ASA High Speed Black

MaterialID MAT0211

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	2026-08-01
Impact	2026-08-01
Izod	Not recorded
Charpy	Not recorded
Stiffness	2026-07-31

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
40

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	5,64 MPa	1,475 MPa	0,262%	9	9/10	OK
Tensile	Flat	24,394 MPa	5,732 MPa	0,235%	10	10/10	OK
Impact	Upright	6,412 kJ/m²	0,904 kJ/m²	0,141%	10	10/10	OK
Impact	Flat	41,504 kJ/m²	1,892 kJ/m²	0,046%	10	10/10	OK
Stiffness	Three-point bend	1984,002 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	48, 22, 53, 31, 38, 29, 41, 34, 34,
Tensile	Flat force inputs (N)	159, 128, 202, 171, 148, 189, 85, 198, 180, 126
Impact	Upright needle inputs (%)	7, 9, 9, 7,5, 8,5, 9,5, 7, 6, 7,5, 8
Impact	Flat needle inputs (%)	58, 55, 51, 54, 57, 54, 49, 56, 50, 52
Stiffness	Revolutions / degrees	2 / 210

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF