Public test session report

Prusa3D Buddy3D Pearl Green PLA Green

MaterialID MAT0221

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	2026-08-04
Impact	2026-08-04
Izod	Not recorded
Charpy	Not recorded
Stiffness	2026-08-04

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
40

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	8,835 MPa	3,152 MPa	0,357%	9	9/10	OK
Tensile	Flat	48,85 MPa	4,085 MPa	0,084%	10	10/10	OK
Impact	Upright	5,96 kJ/m²	0,75 kJ/m²	0,126%	10	10/10	OK
Impact	Flat	13,104 kJ/m²	0,873 kJ/m²	0,067%	10	10/10	OK
Stiffness	Three-point bend	3237,057 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	76, 48, 62, , 21, 74, 51, 90, 49, 46
Tensile	Flat force inputs (N)	320, 304, 323, 347, 309, 288, 344, 353, 319, 269
Impact	Upright needle inputs (%)	8, 8, 7, 7,5, 7,5, 6, 6, 9, 7,5, 7
Impact	Flat needle inputs (%)	16, 17, 15, 17, 17, 16, 14, 16, 17, 15
Stiffness	Revolutions / degrees	1 / 210

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF