Public test session report

Spectrum The Filament Vivid Red PLA Hight Temp Red

MaterialID MAT0224

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-04 18:10:39

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	2026-08-13
Impact	2026-08-13
Izod	Not recorded
Charpy	Not recorded
Stiffness	2026-08-11

Rigid test status
Partial

Rigid result modules
4/6

Rigid specimen/result records
40

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	2,563 MPa	0,48 MPa	0,187%	9	9/10	OK
Tensile	Flat	22,241 MPa	7,154 MPa	0,322%	10	10/10	OK
Impact	Upright	3,632 kJ/m²	1,08 kJ/m²	0,297%	10	10/10	OK
Impact	Flat	11,076 kJ/m²	2,718 kJ/m²	0,245%	10	10/10	OK
Stiffness	Three-point bend	2084,884 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	13, 18, 18, 21, 15, 21, 14, 17, 13,
Tensile	Flat force inputs (N)	176, 150, 104, 129, 171, 211, 118, 98, 210, 79
Impact	Upright needle inputs (%)	1, 4, 5, 5,5, 5, 5, 5, 5,5, 4, 5
Impact	Flat needle inputs (%)	14, 13, 10, 13, 13, 13, 12,5, 18, 20, 9
Stiffness	Revolutions / degrees	2 / 165

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF